电工钢硅钢片 35W550

电工钢硅钢片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example:

电工钢硅钢片本文件按照 GB/T 1.1—2020《标准化工作导则 部分：标准化文件的结构和起草规则》的规定起草。本文件代替 Q/BQB 485－2020。本文件与 Q/BQB 485-2020 相比，主要修改内容如下：— 新增了普通型 Q、华尔网附近高磁极化强度型 QG、华尔网附近磁畴细化型 RK 产品牌号；— 补充配电变压器专用和耐热刻痕磁畴细化两个类型产品；— 补充 B18P070、华尔网附近B20P075、华尔网附近B23P080、华尔网附近B27P085、华尔网附近B27P120、华尔网附近B30P090 六个高磁极化强度型产品和B18R055、华尔网附近B18R060、华尔网附近B20R060、华尔网附近B20R065、华尔网附近B23R070 五个磁畴细化型产品；— 依据 IEC 文件（IEC 6040-8-7 Edition 5.0 2020-09），对单片法（SST）磁性能检测数据转换规则进行调整；— 补充无 Cr 环保涂层产品相关规定；— 修改了钢带的浪高标准。请注意本文件的某些内容可能涉及 。本文件的发布机构不承担识别 的责任。本文件由宝山钢铁股份有限公司硅钢事业部和制造管理部提出。本文件由宝山钢铁股份有限公司硅钢事业部、华尔网附近制造管理部和武钢有限联合起草。本文件所代替的历次版本发布情况为：Q/BQB 485－2007，Q/BQB 485－2014，Q/BQB 485－2016，Q/BQB485－2018，Q/BQB 485－2020。